Hardness below 90A, 3-4 hours at 80℃-90℃ Hardness below 95A, 3-4 hours at 90℃-100℃ When drying, low hardness specification should avoid high temperature and long time for high temperature will cause stick agglomeration and long time drying will make it yellowish Injection molding temperature reference (Unit ℃ ) Model/Specification C1 Feed Section C2 Compression Section C3 Metering Section Nozzle 85A 175 180 185 190 95A 180 185 190 195 64D 190 195 200 205 72D 195 205 210 215 Extrusion molding temperature reference (Unit ℃ ) Model/Specification C1 Feed Section C2 Compression Section C3 Metering Section Nozzle 75A 170 180 180 190 85A 180 185 190 195 95A 185 190 195 200 Characteristic Comparison Model/Specification S100 E300 B400 S600 B700 Transparency Good Excellent Excellent Fair Excellent Hydrolytic Stability Fair Excellent Excellent Fair Good Heat Resistance Good Fair Excellent Good Good Oil Resistance Good Fair Excellent Good Good Low Temperature Resistance Good Excellent Excellent Excellent Good Moldability Good Fair Good Excellent Fair Abrasion Resistance Good Fair Good Excellent Good

Standard Specification Physical Properties ASTM DIN ISO Comparability Specific Gravity D-792 53479 2781 All Comparability Hardness D-2240 53505 868 All Comparability MFI D-1238 53735 1133 All Comparability if 2.16kg Tensile Strength D-412 53455 37 All comparable Flexural Modulus D-790 53452 178 ISO and ASTM Comparable Tear Strength D-624 53515 34 All comparable Mold Shrinkage D-955 53464 294 All Comparable IZOD Impact Strength D-256 53453 180 ASTM and ISO not Comparable Abrasion Loss D-5963 53516 4649 All Comparable Unit Convension Table Bar Mpa Psi kg/cm2 N/mm2 1 0.1 14.5 1 0.1 10 1 145 10 1 0.07 0.007 1 0.07 0.007 Hardness A、HardnessD Table